S205
2015-06-11 08:59:25 Origin： Remark：0 Click：
Specifications S205 Round bar, Plate S205 Flat bar Austentic Steel Remelted, S205 Sheet ESR Blooming, Hot forging, Rolling, Heat treatment
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL DATASHEET - BS S205
MATERIAL CATEGORY - Aerospace "S" Series alloy steel
MATERIAL SPECIFICATIONS - BS EN 3890-2002, BS EN 2344-2001, BS EN 3146-2001
Inventory & Stock available - Diameter 3mm 205mm
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.15
Silicon, Si (％): 0.20 ~ 1.00
Manganese, Mn (％): 0.50 ~ 2.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Silicon, Si (％): 0.20 ~ 1.00
Manganese, Mn (％): 0.50 ~ 2.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 7.50 ~ 9.00
Molybdenum, Mo (％): -
Nickel, Ni (％): 7.50 ~ 9.00
Molybdenum, Mo (％): -
Niobium, Nb/Ti (%): -
HEAT TREATMENT AND MECHANICAL PROPERTIES
Heat treatment temperature and cooling: Solution treatment
Tensile strength, Rm ≥ MPa: 520
Tensile strength, Rm ≥ MPa: 520
Yield strength, Rp0.2 ≥ MPa: 205
Elongation, A5 (%) ≥: 40.0
Hardness ≤HBW: -
Elongation, A5 (%) ≥: 40.0
Hardness ≤HBW: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
FORMS & DIMENSIONS
Round bar / Wire rod (diameter1): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 550mm
Heavy/middle plate via hot rolled: T6 - 300mm X W50 - 1000mm X L1000-12000mm
Round bar / Wire rod (diameter1): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 550mm
Heavy/middle plate via hot rolled: T6 - 300mm X W50 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 300mm X L
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Hot search：S205
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1