S525
2015-06-12 15:11:44 Origin： Remark：0 Click：
Specifications S525 Ex-stock, S525 Chemical, S525 Properties from steelmaking, Electroslag remelting, Blooming, Ultrasonic testing, Hot forging & Rolling, Heat treatment, Cold working, Straightening. We also possess advanced precision machining equipments for further processing. Please contact us for the specific enquiry today.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - BS S525
MATERIAL CATEGORY: Aerospace "S" Series alloy steel
MATERIAL SPECIFICATIONS: BS EN 3890-2002, BS EN 2344-2001, BS EN 3146-2001
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): 0.20 ~ 1.00
Mn (％): 0.50 ~ 2.00
P (％)≤: 0.035
S (％)≤: 0.025
Cr (％): 17.0 ~ 19.0
Ni (％): 9.00 ~ 11.0
Mo (％): ≤ 1.00
Si (％): 0.20 ~ 1.00
Mn (％): 0.50 ~ 2.00
P (％)≤: 0.035
S (％)≤: 0.025
Cr (％): 17.0 ~ 19.0
Ni (％): 9.00 ~ 11.0
Mo (％): ≤ 1.00
Nb/Ti (%): Nb 10X C ~ 1.00
HEAT TREATMENT AND MECHANICAL PROPERTIES
Heat treatment temperature and cooling: Solution treatment
Tensile strength, σb≥/MPa: 520
Tensile strength, σb≥/MPa: 520
Yield strength, σ0.2≥/MPa: 205
Elongation, δ5 (%)≥: 40.0
Hardness ≤HBW: -
Elongation, δ5 (%)≥: 40.0
Hardness ≤HBW: -
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by BEF + AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 4000mm
Sheet steel via cold rolled: T0.5 - 3mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200 mm, with wall thickness ranging from 15 to 350 mm.
Sheet steel via cold rolled: T0.5 - 3mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200 mm, with wall thickness ranging from 15 to 350 mm.
Hot search：S525
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1