Precipitation Steel Custom 455 Round bar, plate and forgings S45500 Electroslag melting, Hot Forging, Rolling, Heat treatment, Cold worked
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATASHEET - Custom 455
MATERIAL CATEGORY: Precipitation hardening stainless steel
MATERIAL SPECIFICATIONS: ASTM A564, A705
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 7.50 ~ 9.50
Molybdenum, Mo (％): ≤ 0.50
Copper, Cu (％): 1.50 ~ 2.50
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 7.50 ~ 9.50
Molybdenum, Mo (％): ≤ 0.50
Copper, Cu (％): 1.50 ~ 2.50
Titanium, Ti (%): 0.80 ~ 1.40
Nb+Ta (%): 0.10 ~ 0.50
MECHANICAL PROPERTIES AFTER HEAT TREATMENT
Condition: H900
Form of Steel: bar, forging
Tensile stength, Rm / MPa: 1620
Yield strength, Rp0.2 / MPa: 1520
Elongation, A5 (％): 8.0
Reduction of area, Z (％): 30.0
Hardness HRC: ≥47
Tensile stength, Rm / MPa: 1620
Yield strength, Rp0.2 / MPa: 1520
Elongation, A5 (％): 8.0
Reduction of area, Z (％): 30.0
Hardness HRC: ≥47
Condition: H950
Tensile stength, Rm / MPa: 1520
Yield strength, Rp0.2 / MPa: 1410
Elongation, A5 (％): 10
Reduction of area,ψ (％): 40
Hardness, HRC: ≥44
Tensile stength, Rm / MPa: 1520
Yield strength, Rp0.2 / MPa: 1410
Elongation, A5 (％): 10
Reduction of area,ψ (％): 40
Hardness, HRC: ≥44
Condition: H1000
Tensile stength, Rm / MPa: 1410
Yield strength, Rp0.2 / MPa: 1280
Elongation, A5 (％): 10
Reduction of area, Z (％): 40
Hardness, HRC: ≥40
Yield strength, Rp0.2 / MPa: 1280
Elongation, A5 (％): 10
Reduction of area, Z (％): 40
Hardness, HRC: ≥40
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / EAF VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
The alloy is usually produced by BEF + AOD / EAF VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Automobile parts, exhaust pipe, Electronics, Turbine motor blade.
Bolt and nuts, Valve sets, Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 600mm
Square bar / Flat bar: 8 ~ 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Square bar / Flat bar: 8 ~ 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1