AMS 5656
2015-07-01 09:04:20 Origin： Remark：0 Click：
Austenitic Stainless Steel AMS 5656, a Chromium - Nickel - Manganese Steel, S21904 Round bar, flat bar, plate and forgings Heat treatment.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
Technical Data Sheet - AMS 5656
Material Category - Austenitic Stainless Steel bar
Technical standards - SAE AMS 5656D
Chemical Compositions (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 8.00 ~ 10.0
Phosphorus, P (％)≤: 0.060
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 19.0 ~ 21.0
Nickel, Ni (％): 5.50 ~ 7.50
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.15 ~ 0.40
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 8.00 ~ 10.0
Phosphorus, P (％)≤: 0.060
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 19.0 ~ 21.0
Nickel, Ni (％): 5.50 ~ 7.50
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.15 ~ 0.40
Tensile strength, Rm / MPa: 655 min.
Yield strength, Rp0.2 / MPa: 330 min.
Elongation, A5 (％): 30 min.
Reduction of area, Z (％): -
Elongation, A5 (％): 30 min.
Reduction of area, Z (％): -
Hardness (HBW): -
Hardness | HRB: -
Cold bending property: None
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter1): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 5000mm
Square bar / Flat bar: 10mm to 800mm
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Hollow bar / forging tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Hollow bar / forging tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：Nitronic 40
Last page：Nitronic 33 / S24000
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1