Nitronic 32 & XM-28
2015-07-02 09:34:02 Origin： Remark：0 Click：
Description Nitronic 32 Inventory, Suppliers Nitronic 32 Ex-stock, Stocklist Nitronic 32 Bar, Wire rod, Sheet - steelmaking, Electroslag melting, Blooming, Ultrasonic test,Hot forging, Rolling, Heat treatment, Nitronic 32 Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - ASTM A276, A580 or By agreement.
TECHNICAL DATA SHEET - Grade Nitronic 32 & XM-28
MATERIAL CATEGORY - Austenitic Stainless Steel
TECHNICAL SPECIFICATIONS - ASTM A276, A580
MELTING PROCESS - Consumable electrode remelted steel
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
STOCKLIST & INVENTORY: Diameter 20 ~ 110mm
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.15
Si (％): ≤ 1.00
Mn (％): 11.0 ~ 14.0
P (％)≤: 0.060
S (％)≤: 0.030
Cr (％): 16.5 ~ 19.5
Ni (％): 0.50 ~ 2.50
Mo (％): -
N (％): 0.20 ~ 0.45
MATERIAL CATEGORY - Austenitic Stainless Steel
TECHNICAL SPECIFICATIONS - ASTM A276, A580
MELTING PROCESS - Consumable electrode remelted steel
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
STOCKLIST & INVENTORY: Diameter 20 ~ 110mm
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.15
Si (％): ≤ 1.00
Mn (％): 11.0 ~ 14.0
P (％)≤: 0.060
S (％)≤: 0.030
Cr (％): 16.5 ~ 19.5
Ni (％): 0.50 ~ 2.50
Mo (％): -
N (％): 0.20 ~ 0.45
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Annealed
Tensile strength, σb/MPa: 760 min.
Yield strength, σ0.2/MPa: 420 min.
Elongation, δ (％): 50 min.
Reduction of area, ф (％): 70.0
Elongation, δ (％): 50 min.
Reduction of area, ф (％): 70.0
Hardness (HBW): -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter1): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Round bar / Wire rod (Diameter1): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search：Nitronic 32 & XM-28
Previous page：BS S65
Last page：Grade 253MA /S30815
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1