X60NiMnCr13-5-3
2015-07-09 13:42:08 Origin： Remark：0 Click：
X60NiMnCr13-5-3 is for fastener material assembly of light alloy components at high temperatures Working, Stock Available X60NiMnCr13-5-3 Round bar, ESR ingot, Cold worked
TECHNICAL DATA SHEET - X60NiMnCr13-5-3
MATERIAL CATEGORY: Aerospace "S" Series alloy steel
STOCK & INVENTORY: Round bar Diam.20 ~ 150mm, ESR ingot.
MELTING PROCESS - Consumable electrode remelted
HS Code for Customs - 7228 4000 / 7228 5000 / 7228 6000
MATERIAL SPECIFICATIONS: BS EN 3890-2002, BS EN 2344-2001, BS S131 - 1977
HS Code for Customs - 7228 4000 / 7228 5000 / 7228 6000
MATERIAL SPECIFICATIONS: BS EN 3890-2002, BS EN 2344-2001, BS S131 - 1977
TYPICAL CHEMICAL COMPOSITIONS (mass fraction - %)
Carbon, C (％): 0.55 ~ 0.70
Silicon, Si (％): 0.20 ~ 0.50
Mangnese, Mn (％): 3.50 ~ 5.50
Phosphorus, P (％) ≤: 0.035
Sulfuer, S (％) ≤: 0.025
Chromium, Cr (％): 3.00 ～ 4.00
Nickel, Ni (％): 11.0 ～ 14.0
Molybdenum, Mo (％): ≤ 0.50
Silicon, Si (％): 0.20 ~ 0.50
Mangnese, Mn (％): 3.50 ~ 5.50
Phosphorus, P (％) ≤: 0.035
Sulfuer, S (％) ≤: 0.025
Chromium, Cr (％): 3.00 ～ 4.00
Nickel, Ni (％): 11.0 ～ 14.0
Molybdenum, Mo (％): ≤ 0.50
Niobium, Titanium, Nb/Ti (%): -
Others (％): W ≤ 1.00, V ≤ 0.25
TYPICAL MECHANICAL PROPERTIES
Condition: solution annealed
Tensile strength, Rm ≥ MPa: 620
Yield strength, Rp0.2 ≥ MPa: 300
Elongation, A5 ≥ (%): 40.0
Yield strength, Rp0.2 ≥ MPa: 300
Elongation, A5 ≥ (%): 40.0
Impact strength, AKu ≥ J: 300 min.
Hardness HBS: -
Hardness HBS: -
Condition: work hardened
Tensile strength, Rm ≥ MPa: 950
Yield strength, Rp0.2 ≥ MPa: 740
Elongation, A5 ≥ (%): 30
Yield strength, Rp0.2 ≥ MPa: 740
Elongation, A5 ≥ (%): 30
AKv ≥ J: -
Hardness HBS: -
Hardness HBS: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：X60NiMnCr13-5-3
Previous page：S114 /EN 16
Last page：BS 304S71
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1