AMS 5655 is ESR high Quality Martensitic Stainless Steel, AISI 422, EN 1.4935, SUH616, ASTM B4B, typically used for parts requiring strength and oxidation resistance up to 538 °C.
MATERIAL TECHNICAL DATASHEET - Grade AMS 5655
MATERIAL CATEGORY - Martensitic high content chromium round bar and forge piece
MATERIAL SPECIFICATIONS - SAE AMS 5655E
INVENTORY LIST - Round bar diam. 30mm ~ 230mm, Flat bar 102 X 204mm
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 11.0 ~ 13.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Tungsten, W (％): 0.90 ~ 1.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 11.0 ~ 13.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Tungsten, W (％): 0.90 ~ 1.25
Vanadium, V (%): 0.20 ~ 0.30
Copper, Cu, (%): ≤ 0.50
MECHANICAL PROPERTIES & HEAT TREATMENT PRACTICE
Condition of heat treatment: Annealed
Tensile strength, σb ≥/MPa: -
Yield strength, σ0.2 ≥/MPa:-
Yield strength, σ0.2 ≥/MPa:-
Elongation, δ ≥(％): -
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤248
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤248
Condition of heat treatment: T, middle tempered
Tensile strength, σb ≥/MPa: -
Yield strength, σ0.2 ≥/MPa:-
Yield strength, σ0.2 ≥/MPa:-
Elongation, δ ≥(％): -
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤285
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤285
Condition of heat treatment: HT 1022℃ ~ 1050℃ air or oil cooled, ≥620℃ X 2H, tempered
Tensile strength, σb ≥/MPa: 965
Yield strength, σ0.2 ≥/MPa: 760
Yield strength, σ0.2 ≥/MPa: 760
Elongation, δ ≥(％): 13.0
Reduction of area, ф ≥(％): 30.0
Hardness | HRS: 302 ~ 352
Reduction of area, ф ≥(％): 30.0
Hardness | HRS: 302 ~ 352
Condition of heat treatment: H 1022℃ ~ 1050℃ air or oil cooled, ≥677℃ X 2H, tempered
Tensile strength, σb ≥/MPa: 825
Yield strength, σ0.2 ≥/MPa: 585
Yield strength, σ0.2 ≥/MPa: 585
Elongation, δ ≥(％): 17.0
Reduction of area, ф ≥(％): 35.0
Hardness | HRS: 241 ~ 285
Reduction of area, ф ≥(％): 35.0
Hardness | HRS: 241 ~ 285
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and Tempered
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and Tempered
PRODUCT PROFILE & DIMENSIONS
Round bar: Diameter 5.5mm to 650mm
Round bar: Diameter 5.5mm to 650mm
Wire rod: 5.5 ~ 12mm
Square bar / Flat bar: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Square bar / Flat bar: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1