18Mn18Cr
2014-09-19 11:28:59 Origin: Remark:0 Click:
18Mn18Cr Specifications, 18Mn18Cr Datasheet, 18Mn18Cr Manufacturers, 18Mn18Cr Bar Forging Ex-stock & Plate Heat treatment Machined, Rod Exporters Ex-stock Sale ASTM A289.
TECHNICAL SPECIFICATIONS: ASTM A289 18Mn-18Cr & 18Mn18Cr & 18Cr-18Mn
MATERIAL CATEGORY: 18Mn-18Cr Austenitic steel, nonmagnetic alloy
Features - ASTM A289/A289M 18Mn-18Cr
Non-magnetic stainless steel reduces the losses in the ring that are caused by eddy currents and thermal stresses. The ring is cold formed to provide the highest yield strength and to ensure plastic deformation does not occur during operation.
TECHNICAL SPECIFICATIONS
ASTM A289 / A289M
CHEMICAL COMPOSITIONS (WEIGHT %)
Carbon (%): 0.10 max
Manganese (%): 17.5 ~ 20.0
Phosphorus (%): 0.060 max
Sulfur (%): 0.015 max
Silicon (%): 0.80 max
Nickel (%): 2.00 max
Chromium (%): 17.5 ~ 20.0
Nitrogen (%): 0.45 ~ 0.80
Titanium (%): 0.10 max
Aluminum (%): 0.04 max
Vanadium (%): 0.25 max
Manganese (%): 17.5 ~ 20.0
Phosphorus (%): 0.060 max
Sulfur (%): 0.015 max
Silicon (%): 0.80 max
Nickel (%): 2.00 max
Chromium (%): 17.5 ~ 20.0
Nitrogen (%): 0.45 ~ 0.80
Titanium (%): 0.10 max
Aluminum (%): 0.04 max
Vanadium (%): 0.25 max
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Grade 1
Tensile Strength,min,MPa | 1000
0.2% Yield Strength,min,MPa | 930
Elongation in 50 mm,min, | % : 28.0
Reduction of Area, min, % : 60.0
Charpy V-Notch energy: 95
Grade 2
Tensile Strength,min,MPa | 1070
0.2% Yield Strength,min,MPa | 1000
Elongation in 50 mm,min, | %: 25.0
Reduction of Area, min, % : 55.0
Charpy V-Notch energy, 88
Grade 3
Tensile Strength,min,MPa | 1140
0.2% Yield Strength,min,MPa | 1105
Elongation in 50 mm,min, | %: 20.0
Reduction of Area, min, % : 50.0
Charpy V-Notch energy, 81
Grade 4
Tensile Strength,min,MPa | 1170
0.2% Yield Strength,min,MPa | 1140
Elongation in 50 mm,min, | %: 19.0
Reduction of Area, min, % : 48.0
Charpy V-Notch energy, 79
Grade 5
Tensile Strength,min,MPa | 1205
0.2% Yield Strength,min,MPa | 1170
Elongation in 50 mm,min, | %: 17.0
Reduction of Area, min, % : 45.0
Charpy V-Notch energy, 75
Grade 6
Tensile Strength,min,MPa | 1275
0.2% Yield Strength,min,MPa | 1240
Elongation in 50 mm,min, | %: 14.0
Reduction of Area, min, % : 40.0
Charpy V-Notch energy, 68
Grade 7
Tensile Strength,min,MPa | 1345
0.2% Yield Strength,min,MPa | 1310
Elongation in 50 mm,min, | %: 12.0
Reduction of Area, min, % : 35.0
Charpy V-Notch energy, 54
Grade 8
Tensile Strength,min,MPa | 1380
0.2% Yield Strength,min,MPa | 1345
Elongation in 50 mm,min, | %: 10.0
Reduction of Area, min, % : 30.0
Charpy V-Notch energy, 47
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL us or call our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search:18Mn18Cr
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1