TECHNICAL DATA SHEET - Grade AISI 301L
MATERIAL CATEGORY: 17Cr-7Ni Austenitic steel
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
AVAILABILITY
Round bar / flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): 5.00 ~ 8.00
Mo (％): -
N (&): ≤ 0.20
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): 5.00 ~ 8.00
Mo (％): -
N (&): ≤ 0.20
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: Plate,sheet, strip
Tensile strength, σb/MPa: 550
Yield strength, σ0.2/MPa: 220
Elongation, δ (％): 45.0
Reduction of area, ф(％): -
Elongation, δ (％): 45.0
Reduction of area, ф(％): -
Hardness (HBW): 241
Hardness | HRB: 100
Cold bending property: N
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut.
Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL us or call our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：301L
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1