300M Alloy / AMS 6419
2015-09-23 10:52:59 Origin： Remark：0 Click：
Specification 300M Forging block, Round bar, Flat bar, steelmaking, ESR / VAR, Blooming, AMS 6419 Forging, Rolling, Heat treatment, Cold worked
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION - 300M Alloy & AMS 6419
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.38 ~ 0.46
Silicon, Si (％): 1.45 ~ 1.80
Manganese, Mn (％): 0.60 ~ 0.90
Phosphorus, P (％) ≤: 0.010
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 0.70 ～ 0.95
Nickel, Ni (％): 1.65 ~ 2.00
Molybdenum, Mo (％): 0.30 ~ 0.65
Silicon, Si (％): 1.45 ~ 1.80
Manganese, Mn (％): 0.60 ~ 0.90
Phosphorus, P (％) ≤: 0.010
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 0.70 ～ 0.95
Nickel, Ni (％): 1.65 ~ 2.00
Molybdenum, Mo (％): 0.30 ~ 0.65
Copper, Cu (%): ≤ 0.35
Vanadium, V (%): 0.05 ~ 0.10
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bar, plate, sheet, forging
Condition: Normalized, hardened and double tempered
Tensile strength, σb/MPa: 1930 min.
Yield strength, σ0.2/MPa: 1580 min.
Elongation, δ (％): 7.0 min.
Reduction of area, ф (％): -
Elongation, δ (％): 7.0 min.
Reduction of area, ф (％): -
Hardness (HBW): -
APPLICATION FIELD
Aircraft landing gear, High strength bolts, Airframe parts, Driveshafts
PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter1): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：300M Alloy /AMS 6419
Previous page：ASTM B536 N08330
Last page：K44220
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1