Ferralium 255 datasheet,Ferralium 255 Chemical,S32550 Ring forging,Ferralium 255 Bar, Wire rod, sheet - steelmaking, ESR, Blooming,Forging, Rolling,Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
TECHNICAL SPECIFICATION DATASHEET - ASTM Ferralium 255
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Duplex stainless steel
Technical standards: ASTM A479
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.040
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 24.0 ~ 27.0
Ni (％): 4.50 ~ 6.50
Mo (％): 2.90 ~ 3.90
N (%): 0.10 ~ 0.25
Cu (%): 1.50 ~ 2.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: round bar
Condition: annealed
Tensile strength, σb/MPa: 750 min.
Yield strength, σ0.2/MPa: 500 min.
Elongation, δ(％): 25 min.
Reduction of area, ф(％): -
Hardness (HBW): -
APPLICATION FIELD
Food processing equipment
Hydrometallurgy, heat exchangers
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
Tall oil distillation columns and equipment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
MATERIAL CATEGORY: Duplex stainless steel
Technical standards: ASTM A479
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.040
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 24.0 ~ 27.0
Ni (％): 4.50 ~ 6.50
Mo (％): 2.90 ~ 3.90
N (%): 0.10 ~ 0.25
Cu (%): 1.50 ~ 2.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: round bar
Condition: annealed
Tensile strength, σb/MPa: 750 min.
Yield strength, σ0.2/MPa: 500 min.
Elongation, δ(％): 25 min.
Reduction of area, ф(％): -
Hardness (HBW): -
APPLICATION FIELD
Food processing equipment
Hydrometallurgy, heat exchangers
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
Tall oil distillation columns and equipment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Previous page：7-Mo Plus
Last page：3RE60 /S31500
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1