Specifications CA6NM datasheet, ASTM CA6NM Chemical,Grade CA6NM Mechanical properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. We also possess the advanced precision machining equipments for further processing, just let us know what you inquire.
TECHNICAL SPECIFICATION - ASTM CA6NM
MATERIAL CATEGORY: Martensitic stainless steel
Technical standards: ASTM A276, A473, A479
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (%): ≤ 0.05
Si (%): ≤ 0. 60
Mn (%): 0.50 ~ 1.00
P (%)≤: 0.030
S (%)≤: 0.030
Cr (%): 11.5 ~ 14.0
Ni (%): 3.50 ~ 5.50
Mo (%): 0.50 ~ 1.00
N (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Forge piece, bar
Condition: Tempered
TS, σb/MPa: 795 Min.
YS, σ0.2/MPa: 620 Min.
Elongation, δ(%): 15 Min.
Reduction of area, ф(%): 45 Min.
Hardness (HBW): -
APPLICATION FIELD
Food processing equipment
Hydrometallurgy, heat exchangers
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
Tall oil distillation columns and equipment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineer, Email: sales@ccsteels.com
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T60 ~ 400mm X W100 - 1000mm X L1000 - 6000mm
Sheet steel via cold rolled: T1.0 - 3mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
MATERIAL CATEGORY: Martensitic stainless steel
Technical standards: ASTM A276, A473, A479
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (%): ≤ 0.05
Si (%): ≤ 0. 60
Mn (%): 0.50 ~ 1.00
P (%)≤: 0.030
S (%)≤: 0.030
Cr (%): 11.5 ~ 14.0
Ni (%): 3.50 ~ 5.50
Mo (%): 0.50 ~ 1.00
N (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Forge piece, bar
Condition: Tempered
TS, σb/MPa: 795 Min.
YS, σ0.2/MPa: 620 Min.
Elongation, δ(%): 15 Min.
Reduction of area, ф(%): 45 Min.
Hardness (HBW): -
APPLICATION FIELD
Food processing equipment
Hydrometallurgy, heat exchangers
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
Tall oil distillation columns and equipment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineer, Email: sales@ccsteels.com
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T60 ~ 400mm X W100 - 1000mm X L1000 - 6000mm
Sheet steel via cold rolled: T1.0 - 3mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Hot search:CA6NM
Previous page:44LN /S31200
Last page:XC100
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1