Material specification Type 634 datasheet,Type 634 Chemical,Type 634 Ring forging, Bar, Wire rod, sheet - steelmaking,ESR,Blooming,Type 634 Forging,Rolling, Type 634 Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
TECHNICAL DATA SHEET - AM-355 & Type 634
MATERIAL CATEGORY: Precipitation hardening stainless steel
Technical standards: ASTM A693
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.10～0.15
Si (％): ≤ 0.50
Mn (％): 0.50 ～ 1.25
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ～ 16.0
Ni (％): 4.00 ～ 5.00
Mo (％): 2.50 ～ 3.25
Other (％): N 0.07 ～ 0.13
Si (％): ≤ 0.50
Mn (％): 0.50 ～ 1.25
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ～ 16.0
Ni (％): 4.00 ～ 5.00
Mo (％): 2.50 ～ 3.25
Other (％): N 0.07 ～ 0.13
MECHANICAL PROPERTIES
APPLICATION FIELD
Form: plate,sheet,strip
Condition: H850
σb/MPa: 1310
σ0.2/MPa: 1140
δ(％): 10
ф(％): -
δ(％): 10
ф(％): -
Hardness | HRB: -
Form: plate,sheet,strip
Condition: H1000
σb/MPa: 1170
σ0.2/MPa: 1030
δ(％): 12
ф(％): -
δ(％): 12
ф(％): -
Hardness | HRB: ≥37
Form: forge piece
Condition: H1000
σb/MPa: 1170
σ0.2/MPa: 1070
σ0.2/MPa: 1070
δ(％): 12
ф(％): 25
Hardness | HRB: ≥37
ф(％): 25
Hardness | HRB: ≥37
Good resistance to chloride stress-corrosion cracking.
Food processing equipment
Hydrometallurgy, heat exchangers
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
Tall oil distillation columns and equipment
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. - Email: lh.steel@hotmail.com
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1