Specifications PH15-7Mo Datasheet, PH15-7Mo Chemical, PH15-7Mo Properties from Steelmaking, ESR melted,Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. Technical specification - ASTM A564, A705. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire
MATERIAL DATASHEET - Grade PH15-7Mo
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Precipitation hardening stainless steel
Technical standards - ASTM A564, A705
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.09
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 14.0 ~ 16.0
Ni (％): 6.50 ~ 7.75
Mo (％): 2.00 ~ 3.00
Al (％): 0.75～1.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bar, forge piece
Condition: TH1050
Tensile strength, σb/MPa: 1240
Yield strength, σ0.2/MPa: 1180
Elongation, δ(％): 12.0
Reduction of area, ф(％): 25.0
Hardness | HRB: -
APPLICATION FIELD
Food processing equipment
Hydrometallurgy, heat exchangers
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
Tall oil distillation columns and equipment
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W60 - 1200mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
MATERIAL CATEGORY - Precipitation hardening stainless steel
Technical standards - ASTM A564, A705
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.09
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 14.0 ~ 16.0
Ni (％): 6.50 ~ 7.75
Mo (％): 2.00 ~ 3.00
Al (％): 0.75～1.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bar, forge piece
Condition: TH1050
Tensile strength, σb/MPa: 1240
Yield strength, σ0.2/MPa: 1180
Elongation, δ(％): 12.0
Reduction of area, ф(％): 25.0
Hardness | HRB: -
APPLICATION FIELD
Food processing equipment
Hydrometallurgy, heat exchangers
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
Tall oil distillation columns and equipment
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W60 - 1200mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Hot search：PH15-7Mo
Previous page：38B3
Last page：PH14-8Mo / S14800
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1