PH14-8Mo / S14800
2015-10-15 09:54:35 Origin： Remark：0 Click：
Round bar S14800 Inventory, Wire S14800 Stock list, PH14-8Mo Plate Forgings properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. Technical specification - AMS5601. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
TECHNICAL SPECIFICATION - Grade PH14-8Mo & S14800
MATERIAL CATEGORY: Precipitation hardening stainless steel
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
Technical standards: AMS5601, AMS5603
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.05
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.015
S (％)≤: 0.010
Cr (％): 13.75 ~ 15.0
Ni (％): 7.75 ~ 8.75
Mo (％): 2.00 ~ 3.00
Al (％): 0.75 ~ 1.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/MPa: 1380
Yield strength, σ0.2/MPa: 1240
Elongation, δ (％): 12.0
Reduction of area, ф (％): 25.0
Hardness | HRB: -
APPLICATION FIELD
Food processing equipment, Hydrometallurgy, heat exchangers.
Oil and gas production equipment, Pulp mill bleach systems.
Seawater handling equipment, Tall oil distillation columns and equipment.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 ~ 200mm X W200 ~ 1000mm X L1000 ~ 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.05
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.015
S (％)≤: 0.010
Cr (％): 13.75 ~ 15.0
Ni (％): 7.75 ~ 8.75
Mo (％): 2.00 ~ 3.00
Al (％): 0.75 ~ 1.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/MPa: 1380
Yield strength, σ0.2/MPa: 1240
Elongation, δ (％): 12.0
Reduction of area, ф (％): 25.0
Hardness | HRB: -
APPLICATION FIELD
Food processing equipment, Hydrometallurgy, heat exchangers.
Oil and gas production equipment, Pulp mill bleach systems.
Seawater handling equipment, Tall oil distillation columns and equipment.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 ~ 200mm X W200 ~ 1000mm X L1000 ~ 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Previous page：PH15-7Mo
Last page：Lapelloy / S42300
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1