1.4503
2015-10-23 09:48:24 Origin： Remark：0 Click：
EN 1.4503, Austenitic Stainless Steel Containing high alloy element of 27Ni-23Cr-3Mo. 1.4503 Round bar, Flat bar, Plate ESR melted, Hot rolling, Heat treatment
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL DATASHEET - 1.4503
MATERIAL CATEGORY: Austenitic stainless steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.04
Silicon, Si (％): ≤ 0.75
Manganese, Mn (％): ≤ 0.75
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): 26.0 ~ 28.0
Molybdenum, Mo (％): 2.50 ~ 3.00
Copper, Cu (％): 2.50～3.50
Silicon, Si (％): ≤ 0.75
Manganese, Mn (％): ≤ 0.75
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): 26.0 ~ 28.0
Molybdenum, Mo (％): 2.50 ~ 3.00
Copper, Cu (％): 2.50～3.50
Titanium, Ti (%): 0.40 ~ 0.70
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, Rm ≥ MPa: 575
Yield strength, Rp0.2 ≥ MPa: -
Elongation, A5 ≥ (％): -
Elongation, A5 ≥ (％): -
Reduction of area, Z ≥ (％): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipment
Food processing equipment
Hydrometallurgy, heat exchangers
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Mr Chen, Mr.Jiang - Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Mr Chen, Mr.Jiang - Email: sales@ccsteels.com.
Hot search：1.4503
Previous page：Cronifer 2328 /ASM SS-411
Last page：23MNCD5
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1