Austenitic stainless steel Cronifer 1815 LCSi Round bar, Flat baar, Plate Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - Grade Cronifer 1815 LCSi / S30600
MATERIAL CATEGORY: Austenitic stainless steel
Technical standards: Nonstandards frequently-used alloy
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.018
Silicon, Si (％): 3.70 ~ 4.30
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.020
Chromium, Cr (％): 17.0 ~ 18.5
Nickel, Ni (％): 14.0 ~ 15.5
Molybdenum, Mo (％): ≤ 0.20
Other (％): -
Silicon, Si (％): 3.70 ~ 4.30
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.020
Chromium, Cr (％): 17.0 ~ 18.5
Nickel, Ni (％): 14.0 ~ 15.5
Molybdenum, Mo (％): ≤ 0.20
Other (％): -
MECHANICAL PROPERTIES AT ROOM TEMP.
Tensile strength, σb/≥ MPa: 540
Yield strength, σ0.2/≥ MPa: 240
Elongation, δ ≥(％): 40.0
Elongation, δ ≥(％): 40.0
Reduction of area, ф ≥ (％): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipments.
Food processing equipments, Hydrometallurgy, heat exchangers.
Oil and gas production equipments, Pulp mill bleach systems, Seawater handling equipments.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Previous page：RA 85H / S30615
Last page：25MNDC6
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1