Technical specification of American nonstandard frequently-used austenitic stainless steel alloy MVMA datasheet, MVMA Chemical compositions,mechanical properties from Steelmaking,MVMA ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - MVMA /S30415
MATERIAL CATEGORY: Austenitic stainless steel
Technical standards: Nonstandards frequently-used alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.04~0.05
Si (％): 1.00~2.00
Mn (％): ≤0.80
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 18.0～19.0
Ni (％): 9.00～10.0
Mo (％): -
Other (％): Ce 0.03~0.08, N 0.12~0.18
Si (％): 1.00~2.00
Mn (％): ≤0.80
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 18.0～19.0
Ni (％): 9.00～10.0
Mo (％): -
Other (％): Ce 0.03~0.08, N 0.12~0.18
MECHANICAL PROPERTIES
σb/≥ MPa: 600
σ0.2/≥ MPa: 290
δ ≥(％): 40
δ ≥(％): 40
ф ≥ (％): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
Pulp mill bleach systems
Seawater handling equipments
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
Previous page：304BI /S30424
Last page：18-18 Plus & S28200
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1