S24000
2015-10-30 11:13:22 Origin： Remark：0 Click：
ASTM A276 Specification of Austenitic stainless steel S24000 Round bar, Flat bar, Forgings S24000 ESR Ingot, Hot forging / rolling, Heat treatment
TECHNICAL DATA SHEET - UNS S24000
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic stainless steel
Technical standards: Nonstandards frequently-used alloy
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 0.75
Manganese, Mn (％): 11.5 ~ 14.5
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 2.25 ~ 3.75
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.20 ~ 0.40
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, Rm ≥ MPa: 690
Yield strength, Rp0.2 ≥ MPa: 380
Elongation, A5 ≥ (％): 40.0
Reduction of area, Z ≥ (％): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
Pulp mill bleach systems
Seawater handling equipments
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
MATERIAL CATEGORY: Austenitic stainless steel
Technical standards: Nonstandards frequently-used alloy
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 0.75
Manganese, Mn (％): 11.5 ~ 14.5
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 2.25 ~ 3.75
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.20 ~ 0.40
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, Rm ≥ MPa: 690
Yield strength, Rp0.2 ≥ MPa: 380
Elongation, A5 ≥ (％): 40.0
Reduction of area, Z ≥ (％): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
Pulp mill bleach systems
Seawater handling equipments
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：S24000
Previous page：40NiCrMo10-4
Last page：Nitronic 60
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1