203 EZ / XM-1
2015-11-05 09:32:33 Origin： Remark：0 Click：
Specifications AISI 203EZ Datasheet, XM-1 / 203 EZ Chemical, 203EZ Property from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - 203 EZ & XM-1
MATERIAL CATEGORY: Austenitic stainless steel
Technical standards: Nonstandards frequently-used alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): 5.00 ~ 6.50
P (％)≤: 0.040
S (％)≤: 0.18 ~ 0.35
Cr (％): 16.0 ~ 18.0
Ni (％): 5.00 ~ 6.50
Mo (％): ≤ 0.50
Si (％): ≤ 1.00
Mn (％): 5.00 ~ 6.50
P (％)≤: 0.040
S (％)≤: 0.18 ~ 0.35
Cr (％): 16.0 ~ 18.0
Ni (％): 5.00 ~ 6.50
Mo (％): ≤ 0.50
N (%): -
Cu (％): 1.75 ~ 2.25
Cu (％): 1.75 ~ 2.25
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 425
Yield strength, σ0.2/≥ MPa: 385
Elongation, δ ≥(％): 15.0
Elongation, δ ≥(％): 15.0
Reduction of area, ф ≥ (％): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
Pulp mill bleach systems
Seawater handling equipments
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com.
Previous page：Tenelon / XM-31
Last page：Call-Tough /S20161
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1