AMS 5643
2015-12-08 20:02:51 Origin: Remark:0 Click:
AMS 5643 is aerospace ESR quality martensitic precipitation hardening stainless steel in form of bars, Shaft, Stock list AMS 5643 Flat bars, Valve body via Hot forging, Hot rolling, Heat treated, Straightening, 100% Ultrasonic test, cold machining. Technical specification - AMS 6543.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
RAW MATERIAL TECHNICAL DATASHEET - Grade AMS 5643
MATERIAL CATEGORY - Martensitic stainless steel
INVENTORY & STOCKLIST on hand - Diam.5.5 ~ 400mm
HS CODE - 72221100 / 72221900 / 72222000
Technical standards - AMS 5643F
CHEMICAL COMPOSITION ( Mass weight % )
C (%): ≤ 0.07
Si (%): ≤ 1.00
Mn (%): ≤ 1.00
P (%)≤: 0.030
S (%)≤: 0.015
Cr (%): 15.0~17.50
Ni (%): 3.00 ~ 5.00
Cu (%): 3.00 ~ 5.00
Si (%): ≤ 1.00
Mn (%): ≤ 1.00
P (%)≤: 0.030
S (%)≤: 0.015
Cr (%): 15.0~17.50
Ni (%): 3.00 ~ 5.00
Cu (%): 3.00 ~ 5.00
Nb (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Heat condition: H900 / H1000 / H1050 / H1100 H 1150
Tensile strength, σb/MPa: ≥1310 (+ H900)
Yield strength, σ0.2/MPa: ≥1170
Elongation, δ (%): ≥ 10.0
Reduction of area, ψ (%): ≥ 40.0
Tensile strength, σb/MPa: ≥1310 (+ H900)
Yield strength, σ0.2/MPa: ≥1170
Elongation, δ (%): ≥ 10.0
Reduction of area, ψ (%): ≥ 40.0
Hardness / HRC: ≥40
APPLICATION FIELD
Flue gas desulfurization scrubbers.
Food processing equipment.
Heat exchangers.
Hydrometallurgy.
Oil and gas production equipment.
Pulp mill bleach systems.
Seawater handling equipment.
Tall oil distillation columns and equipment.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + Aged
The alloy is usually produced by AOD / EAF / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + Aged
Heavy/middle plate via hot rolled: T60 - 200mm X W60 - 1200mm X L1000 - 6000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs / tubes / slugs / donuts / cubes / other different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs / tubes / slugs / donuts / cubes / other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1