Description S30452 datasheet, S30452 Chemical, S30452 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
AUSTENITIC DATA SHEET - UNS S30452
MATERIAL CATEGORY - 19Cr-9Ni-N Austenitic steel
MATERIAL SPECIFICTIONS - STM A959 (2004), A276, A312, A632, A176, A580
AVAILABILITY
Black bar / Flat bar / Steel strip / Square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Black bar / Flat bar / Steel strip / Square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 18.0 ~ 20.0
Ni (％): 8.0 ~ 10.0
Mo (％): -
N (&): 0.16 ~ 0.30
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: Plate,sheet, strip
Tensile strength, σb/MPa: 520
Yield strength, σ0.2/MPa: 215
Elongation, δ(％): 45.0
Reduction of area, ф(％): 70
Hardness (HBW): -
Hardness | HRB: -
Cold bending property: N
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 18.0 ~ 20.0
Ni (％): 8.0 ~ 10.0
Mo (％): -
N (&): 0.16 ~ 0.30
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: Plate,sheet, strip
Tensile strength, σb/MPa: 520
Yield strength, σ0.2/MPa: 215
Elongation, δ(％): 45.0
Reduction of area, ф(％): 70
Hardness (HBW): -
Hardness | HRB: -
Cold bending property: N
INVENTORY - hot forged disc, bar
Diameter: 30mm, 40mm, 45mm, 50mm, 65mm, 120mm, 165mm
Quantity: 45000kg
Diameter: 30mm, 40mm, 45mm, 50mm, 65mm, 120mm, 165mm
Quantity: 45000kg
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：S30452
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1