21Cr-10Ni-2Mn Austenitic steel ER308 Round bar, Flat bar, S30880 Plate ESR refined, Blooming, Hot forging, Hot rolling, Heat treatment
MATERIAL SPECIFICATIONS - ASTM ER308 & UNS S30880
MATERIAL CATEGORY: 21Cr-10Ni-2Mn Austenitic steel
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): 0.25 ~ 0.60
Manganese, Mn (％): 1.00 ~ 2.50
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 19.5 ~ 22.0
Nickel, Ni (％): 9.00 ~ 11.0
Molybdenum, Mo (％): -
Silicon, Si (％): 0.25 ~ 0.60
Manganese, Mn (％): 1.00 ~ 2.50
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 19.5 ~ 22.0
Nickel, Ni (％): 9.00 ~ 11.0
Molybdenum, Mo (％): -
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: Plate,sheet,strip
Tensile strength, σb/MPa: 600
Yield strength, σ0.2/MPa: 310
Elongation, δ (％): 40
Reduction of area, ф (％): -
Elongation, δ (％): 40
Reduction of area, ф (％): -
Hardness (HBW): 217
Hardness | HRB: 95
Cold bending property: N
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
Chemical equipment.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Previous page：UNS S30815
Last page：UNS S30880
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1