Description Nitronic 30 Round bar, Inventory Nitronic 30 Plate Nitronic 30 Forgings properties from Steelmaking, ESR melted, Hot forging / rolling, Heat treatment.
TECHNICAL DATA SHEET - Nitronic 30
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic stainless steel
TECHNICAL SPECIFICATIONS - ASTM A276, A580
MELTING PROCESS - Consumable electrode remelted
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
STOCKLIST & INVENTORY: Diameter 80 ~ 110mm
MELTING PROCESS - Consumable electrode remelted
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
STOCKLIST & INVENTORY: Diameter 80 ~ 110mm
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 7.00 ~ 9.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 15.0 ~ 17.0
Nickel, Ni (％): 1.50 ~ 3.00
Molybdenum, Mo (％): -
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 7.00 ~ 9.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 15.0 ~ 17.0
Nickel, Ni (％): 1.50 ~ 3.00
Molybdenum, Mo (％): -
Tungsten, W (%): -
Copper, Cu (%): ≤ 1.00
Titanium, Ti (%): -
Cobalt, Co (%): -
Nitrogen, N (％): 0.15 ~ 0.30
Nitrogen, N (％): 0.15 ~ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, Rm ≥ MPa: 758
Yield strength, Rp0.2 ≥ MPa: 380
Elongation, A5 ≥ (％): 50
Elongation, A5 ≥ (％): 50
Reduction of area, Z ≥ (％): -
Hardness | HRB: B95
APPLICATION FIELD
Tall oil distillation columns and equipments.
Food processing equipments, Hydrometallurgy, heat exchangers.
Oil and gas production equipments, Pulp mill bleach systems, Seawater handling equipments.
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200mm, with wall thickness ranging from 15 to 350 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200mm, with wall thickness ranging from 15 to 350 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Previous page：Nitronic 20
Last page：S20400 / Nitronic 30
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1