F44 / S31254
2016-02-29 10:17:47 Origin: Remark:0 Click:
Specifications ASTM A182 / EN 10088-1 of Steel S31254 / F44 Round bar, flat bar, plate Hot Forging, Hot rolling, Heat treatment, Ultrasonic test, Cold machined.
TECHNICAL SPECIFICATIONS - Grade F44 & S31254
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic stainless steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.020
Silicon, Si (%): ≤ 0.80
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.010
Chromium, Cr (%): 19.5 ~ 20.5
Nickel, Ni (%): 17.5 ~ 18.5
Molybdenum, Mo (%): 6.00 ~ 6.50
Silicon, Si (%): ≤ 0.80
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.010
Chromium, Cr (%): 19.5 ~ 20.5
Nickel, Ni (%): 17.5 ~ 18.5
Molybdenum, Mo (%): 6.00 ~ 6.50
Copper, Cu (%): 0.50 ~ 1.00
Nitrogen, N (%): 0.18 ~ 0.22
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 310
Elongation, δ ≥(%): 35
Elongation, δ ≥(%): 35
Reduction of area, ф ≥ (%): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipments, Food processing equipments.
Hydrometallurgy, heat exchangers, Oil and gas production equipments.
Pulp mill bleach systems, Seawater handling equipments.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified enginners, Email: sales@ccsteels.com
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1