Alloy 926
2016-02-29 10:40:34 Origin: Remark:0 Click:
Specifications 926 /1.4529 datasheet, 926 Chemical, alloy 926/1.4529 mechanical property from Steelmaking,ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. Technical specifications - EN 10088-1.We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
MATERIAL SPECIFICATIONS - Alloy 926
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic stainless steel
CHEMICAL COMPOSITION (WEIGHT %)
C (%): ≤ 0.020
Si (%): ≤ 0.50
Mn (%): ≤ 2.00
P (%)≤: 0.030
S (%)≤: 0.010
Cr (%): 19.0 ~ 21.0
Ni (%): 24.0 ~ 25.0
Mo (%): 6.00 ~ 7.00
Si (%): ≤ 0.50
Mn (%): ≤ 2.00
P (%)≤: 0.030
S (%)≤: 0.010
Cr (%): 19.0 ~ 21.0
Ni (%): 24.0 ~ 25.0
Mo (%): 6.00 ~ 7.00
Cu (%): 0.50 ~ 1.50
N (%): 0.15 ~ 0.25
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treated
σb/≥ MPa: 650~ 850
σ0.2/≥ MPa: 300
δ ≥(%): 35
δ ≥(%): 35
ф ≥ (%): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
Pulp mill bleach systems
Seawater handling equipments
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T60 - 400mm X W80 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Tubings: OD30 - 1500 mm, with wall thickness ranging from 10 to 350 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Tubings: OD30 - 1500 mm, with wall thickness ranging from 10 to 350 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page:F44 / S31254
Last page:ISO X210Cr12
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1