403Cb Blade Steel Forgings, Round bar, Flat bar 403Cb Steelmaking, Stock Available S40300 ESR melted H46 Heat treatment
TECHNICAL DATA SHEET - 403Cb & H46
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Martensitic stainless steel
STOCK AVAILABLE - Round bar Diam. 10 ~ 240mm, Flat bar 50 ~ 220 * 60 ~ 265 * Lmm
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.13 ~ 0.18
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.40 ~ 0.60
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 11.5 ~ 13.0
Nickel, Ni (％): ≤ 0.60
Niobium, Nb (％): 0.15 ~ 0.45
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.40 ~ 0.60
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 11.5 ~ 13.0
Nickel, Ni (％): ≤ 0.60
Niobium, Nb (％): 0.15 ~ 0.45
TYPICAL MECHANICAL PROPERTIES
Tensile strength, Rm ≥ MPa: 828
Yield strength, Rp0.2 ≥ MPa: 725
Elongation, A5 ≥ (％): 17.0
Elongation, A5 ≥ (％): 17.0
Recution of area, Z ≥ (％): 50.0
Hardness | HB: 255 ~ 302
APPLICATION FIELD
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
Pulp mill bleach systems
Seawater handling equipments
PRODUCT DESCRIPTION & DIMENSIONS
The alloy is usually produced by AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and termpered + SRA.
The alloy is usually produced by AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and termpered + SRA.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Pipes / Tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Pipes / Tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：AISI/SAE 6120
Last page：403Cb
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1