SUS304N2
2016-05-12 09:54:53 Origin： Remark：0 Click：
Technical specifications JIS austenitic stainless steel alloy SUS304N2 datasheet, SUS304N2 Chemical compositions, SUS304N2 mechanical properties from Steelmaking, ESR melting, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - JIS G4303 -2005.We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
MATERIAL TECHNICAL DATA SHEET - JIS SUS304N2
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic stainless steel
TECHNICAL SPECIFICATIONS: JIS G4303 -2005
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 2.50
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 18.0～20.0
Ni (％): 7.50~10.5
Mo (％): -
Si (％): ≤ 1.00
Mn (％): ≤ 2.50
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 18.0～20.0
Ni (％): 7.50~10.5
Mo (％): -
N (%): 0.10~0.30
Nb (%): ≤ 0.15
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICE
Condition: solution treated
Heat treatment temperature /℃: 1010~1150
Medium: rapid cooling
σb/≥ MPa: 690
σ0.2/≥ MPa: 345
δ ≥(％): 35
δ ≥(％): 35
ф ≥ (％): 50
Hardness | HB ≤: 217
APPLICATION FIELD
Pulp mill bleach systems
Seawater handling equipments
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by IFF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Hot search：SUS304N2
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1