10705BU
2016-05-12 22:32:28 Origin： Remark：0 Click：
Martensitic Steel 10705BU Turbine blades Steel Round Bar, flat bar 10705BU ESR, Hot Forging Rolling, Heat treated, Cold machined.
MATERIAL DESIGNATION - 10705BU
MATERIAL CATEGORY: Martensitic high content chromium round bar and forging pieces.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MELTING PROCESS - AOD / BEF / EAF + Consumable electrode remelted.
H S CODE For Customs - 72201100 / 72202030 / 72221100 / 72222000 / 72223000
STOCK LIST & INVENTORY - Bright round bar Diameter 20 ~ 210mm
CHEMICAL COMPOSITIONS (mass weight - %)
H S CODE For Customs - 72201100 / 72202030 / 72221100 / 72222000 / 72223000
STOCK LIST & INVENTORY - Bright round bar Diameter 20 ~ 210mm
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Tungsten, W (％): 0.90 ~ 1.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Tungsten, W (％): 0.90 ~ 1.25
Vanadium, V (%): 0.20 ~ 0.30
TYPICAL MECHANICAL PROPERTIES AT RM TEMP.
Condition of heat treatmetn: +A
Tensile strength, TS, σb ≥ MPa: -
Yield strength, YS, σ0.2 ≥ MPa:-
Yield strength, YS, σ0.2 ≥ MPa:-
Elongation, δ5 ≥ (％): -
Reduction of area, RA, ф ≥( ％): -
Hardness | HRS: ≤248
Reduction of area, RA, ф ≥( ％): -
Hardness | HRS: ≤248
Condition of heat treatment: Hardened 1022℃ ~ 1050℃ air or oil cooled, ≥620℃ X 2H, tempered
Tensile strength, σb ≥ MPa: 965
Yield strength, σ0.2 ≥ MPa: 760
Yield strength, σ0.2 ≥ MPa: 760
Elongation, δ5 ≥ (％): 13.0
Reduction of area , ф ≥ (％): 30.0
Hardness | HRS: 302 ~ 352
Reduction of area , ф ≥ (％): 30.0
Hardness | HRS: 302 ~ 352
Condition of heat treatment: Hardened 1022℃ ~ 1050℃ air or oil cooled, ≥677℃ X 2H, tempered
Tensile strength, σb ≥ MPa: 825
Yield strength, σ0.2 ≥ MPa: 585
Yield strength, σ0.2 ≥ MPa: 585
Elongation, δ5 ≥ (％): 17.0
Reduction of area, ф ≥ (％): 35.0
Hardness | HRS: 241 ~ 285
Reduction of area, ф ≥ (％): 35.0
Hardness | HRS: 241 ~ 285
PRODUCT SHAPES & DIMENSIONS
Round bar & Disc (diameter): 5.5 mm to 800 mm
Square bar / Flat bar: 10mm to 550mm
Round bar & Disc (diameter): 5.5 mm to 800 mm
Square bar / Flat bar: 10mm to 550mm
Forged ring: OD200 ~ 1200mm X ID150 ~ 1250mm X H20 ~ 1250mm
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W80- 1200mm X L1000 - 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
Forging piece: stepped shafts, other different shapes based on OEM.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
Hot search：10705BU
Previous page：AISI/SAE TS8127
Last page：SUS304J3
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1