SUS316L
2016-05-16 09:05:23 Origin： Remark：0 Click：
Technical specifications of JIS Austenitic stainless steel SUS316L Round bar, Flat bar, Plate, SUS316L mechanical properties, Heat treatment
MATERIAL DATA SHEET - JIS SUS316L
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic stainless steel
TECHNICAL SPECIFICATIONS: JIS G4303 -2005
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 16.0～18.0
Nickel, Ni (％): 12.0~15.0
Molybdenum, Mo (％): 2.00 ~ 3.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 16.0～18.0
Nickel, Ni (％): 12.0~15.0
Molybdenum, Mo (％): 2.00 ~ 3.00
Nitrogen, N (%): -
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICE
Condition: solution treated
Heat treatment temperature /℃: 1010~1150
Medium: rapid cooling
Tensile strength, Rm ≥ MPa: 480
Yield strength, Rp0.2 ≥ MPa: 175
Elongation, A5 ≥ (％): 40
Elongation, A5 ≥ (％): 40
Reduction of area, ф ≥ (％): 60
Hardness | HB ≤: 217
APPLICATION FIELD
Pulp mill bleach systems, Seawater handling equipments.
Tall oil distillation columns and equipments.
Food processing equipments.
Hydrometallurgy, heat exchangers.
Oil and gas production equipments.
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by IFF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Round bar & Disc: Diam.5.50 ~ 550mm
Flat / Square bar: T10 ~ 350mm X W15 ~ 1200mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：SUS316L
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1