JIS G4303 -2005 of Steel SUS410J1 Round bar, Plate, Sheet, ESR melting, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test.
MATERIAL TECHNICAL DATA SHEET - JIS SUS410J1
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel
TECHNICAL SPECIFICATIONS: JIS G4303 -2005
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.08 ~ 0.18
Silicon, Si (％): ≤ 0.60
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 11.5 ～ 14.0
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 11.5 ～ 14.0
Nickel, Ni (％): ≤ 0.60
Molybdenum, Mo (％): 0.30 ~ 0.60
Molybdenum, Mo (％): 0.30 ~ 0.60
Nitrogen, N (%): -
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICE
Condition: annealed
Heat treatment temperature /℃: 830~900
Medium: rapid cooling or slow cooling
σb/≥ MPa: -
σ0.2/≥ MPa: -
δ ≥(％): -
δ ≥(％): -
ф ≥ (％): -
Hardness | HBW ≤: 200
Condition: Quenched and tempered
Heat treatment temperature /℃: Quenched 970~1020 oil cooled, Tempered 700~750 rapid cooled
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 490
Elongation, δ ≥(％): 20.0
Elongation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): 60
Hardness | HBW ≤: 192
APPLICATION FIELD
Pulp mill bleach systems, Seawater handling equipments.
Tall oil distillation columns and equipments.
Food processing equipments, Hydrometallurgy, heat exchangers.
Oil and gas production equipments.
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT treated.
The alloy is usually produced by IFF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT treated.
Round bar: Diam. 5.5 ~ 550mm
Flat / Square bar: T10 ~ 350mm X W15 ~ 1200mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Hot search：SUS410J1
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1