SUS416
2016-05-31 09:20:31 Origin： Remark：0 Click：
JIS G4303 Specification Martensitic Stainless Steel SUS416 Round bar, Rod, Flat bar, Forgings SUS416, Hot forging, Hot rolling, Heat treatment
MATERIAL DATA SHEET - JIS SUS416
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel
TECHNICAL SPECIFICATIONS: JIS G4303 -2005
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.15
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.25
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.15 min.
Chromium, Cr (％): 12.0～14.0
Manganese, Mn (％): ≤ 1.25
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.15 min.
Chromium, Cr (％): 12.0～14.0
Nickel, Ni (％): ≤ 0.60
Molybdenum, Mo (％): ≤ 0.60
Molybdenum, Mo (％): ≤ 0.60
Nitrogen, N (%): -
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICE
Condition: annealed
Heat treatment temperature /℃: 800~900
Medium: rapid cooling or slow cooling
Tensile strength, Rm ≥ MPa: -
Yield strength, Rp0.2 ≥ MPa: -
Elongation, A5 ≥ (％): -
Elongation, A5 ≥ (％): -
Reduction of area, Z ≥ (％): -
Hardness | HBW ≤: 200
Condition: Quenched and tempered
Heat treatment temperature /℃: Quenched 950~1000 oil cooled, Tempered 700~750 rapid cooled
σb ≥ MPa: 540
σ0.2 ≥ MPa: 345
δ5 ≥ (％): 17
δ5 ≥ (％): 17
ф ≥ (％): 45
Hardness | HBW ≤: 159
APPLICATION FIELD
Pulp mill bleach systems, Seawater handling equipments.
Tall oil distillation columns and equipments, Food processing equipments.
Hydrometallurgy, heat exchangers, Oil and gas production equipments.
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by IFF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Round bar: Diam. 3.0 ~ 550mm
Flat / Square bar: T10 ~ 350mm X W15 ~ 1200mm
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：SUS416
Previous page：AISI/SAE 86B45
Last page：SUS420J1
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1