MATERIAL TECHNICAL DATASHEET - JIS SUS420F2
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Martensitic stainless steel
TECHNICAL SPECIFICATIONS: JIS G4303 -2005
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.26 ~ 0.40
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 12.0～14.0
Ni (％): ≤ 0.60
Mo (%): -
N (%): -
Pb (%): 0.05 ~ 0.30
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICE
Condition: + annealed
Heat treatment temperature /℃: 800~900
Medium: rapid cooling or slow cooling
σb/≥ MPa: -
σ0.2/≥ MPa: -
δ ≥(％): -
ф ≥ (％): -
Hardness | HBW ≤: 235
Condition: Quenched and tempered Heat treatment temperature /℃: Quenched 920~980 oil cooled, Tempered 600~750 rapid cooled
Tensile strengrh, σb/≥ MPa: 740
Yield strength, σ0.2/≥ MPa: 540
Elongation, δ ≥(％): 35.0
Reduction of area, ф ≥ (％): 35
Hardness | HBW ≤: 217
APPLICATION FIELD
Pulp mill bleach systems
Seawater handling equipments
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Round bar: Diam.5.5 ~ 550mm
Flat / Square bar: T10 ~ 350mm X W15 ~ 1200mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Martensitic stainless steel
TECHNICAL SPECIFICATIONS: JIS G4303 -2005
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.26 ~ 0.40
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 12.0～14.0
Ni (％): ≤ 0.60
Mo (%): -
N (%): -
Pb (%): 0.05 ~ 0.30
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICE
Condition: + annealed
Heat treatment temperature /℃: 800~900
Medium: rapid cooling or slow cooling
σb/≥ MPa: -
σ0.2/≥ MPa: -
δ ≥(％): -
ф ≥ (％): -
Hardness | HBW ≤: 235
Condition: Quenched and tempered Heat treatment temperature /℃: Quenched 920~980 oil cooled, Tempered 600~750 rapid cooled
Tensile strengrh, σb/≥ MPa: 740
Yield strength, σ0.2/≥ MPa: 540
Elongation, δ ≥(％): 35.0
Reduction of area, ф ≥ (％): 35
Hardness | HBW ≤: 217
APPLICATION FIELD
Pulp mill bleach systems
Seawater handling equipments
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Round bar: Diam.5.5 ~ 550mm
Flat / Square bar: T10 ~ 350mm X W15 ~ 1200mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：SUS420F2
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1