Description AISI 321 Suppliers, Stocklist AISI 321 Round bar, Inventory AISI 321 Property from Steelmaking, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade AISI 321
MATERIAL CATEGORY - 18Cr-11Ni-Ti Austenitic steel
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / BEF / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / BEF / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
AVAILABILITY
Round bar / flat bar / strip / sheet / forgings / tube
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / strip / sheet / forgings / tube
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 500mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 500mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): 9.00 ~ 12.0
Mo (％): -
Ti (％): 5 X (C + N ) ~ 0.70, N ≤0.10
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): 9.00 ~ 12.0
Mo (％): -
Ti (％): 5 X (C + N ) ~ 0.70, N ≤0.10
MECHANICAL PROPERTIES UNDER FINAL HEAT TREATMENT
Form: Plate,sheet,strip
Condition: annealing
Tensile strength, σb/MPa: 515
Yield strength, σ0.2/MPa: 205
Elongation, δ (％): 40.0
Reduction of area, ф (％): -
Elongation, δ (％): 40.0
Reduction of area, ф (％): -
Hardness | HRB: 95
Form: wire
Condition: annealing
Condition: annealing
Tensile strength, σb/MPa: 515
Yield strength, σ0.2/MPa: 205
Elongation, δ (％): 35.0
Reduction of area, ф (％): 50
Hardness | HRB: -
Yield strength, σ0.2/MPa: 205
Elongation, δ (％): 35.0
Reduction of area, ф (％): 50
Hardness | HRB: -
Cold bending property: N
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
INVENTORY - hot rolled bar, plate, disc
Diameter: 10 - 260mm
Diameter: 10 - 260mm
Plate: T1 - 100mm, W100 - 2000mm
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1