Technical specifications of JIS heat resistance steel alloy SUH309 data sheet, Chemical compositions, SUH309 mechanical properties from Steel making, ESR melting, Hot blooming, SUH309 forging, Hot rolling, SUH309 Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - JIS G4311 -1991.We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
MATERIAL TECHNICAL DATA SHEET - JIS SUH309
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Heat resisting steel Austinite stainless steel
TECHNICAL SPECIFICATIONS: JIS G4311 -1991
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.20
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 22.0 ~ 24.0
Ni (％): 12.0 ~ 15.0
Mo (%): -
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.20
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 22.0 ~ 24.0
Ni (％): 12.0 ~ 15.0
Mo (%): -
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICE
Annealed: -
Annealed: -
Solution treated or Quenching: 1030 ~ 1150, rapid cooled
Ageging treated or Tempering: -
Condition: Solution treated
σb/≥ MPa: 560
σ0.2/≥ MPa: 205
δ ≥(％): 45
ф ≥ (％): 50
Hardness | HBW ≤: 201.
σb/≥ MPa: 560
σ0.2/≥ MPa: 205
δ ≥(％): 45
ф ≥ (％): 50
Hardness | HBW ≤: 201.
Suitable size (Diam. Thickness, Square size): ≤ 180 mm
APPLICATION FIELD
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
APPLICATION FIELD
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
Pulp mill bleach systems
Seawater handling equipments
Tall oil distillation columns and equipments
Seawater handling equipments
Tall oil distillation columns and equipments
Heat-resistant steels are widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
Manufacturing technology - Smelting
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
Manufacturing technology - Smelting
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
PRODUCT DESCRIPTION
Round bar: Diam.1.0 ~ 850mm
Flat / Square bar: T10 ~ 350mm X W15 ~ 1200mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email: lh.steel@hotmail.com
Hot search：SUH309
Previous page：SUH38
Last page：5046H H50460
Total list
Monthly rank
- 39ASTM A565 Gr.616HT
- 37X35CrMo17
- 30ASTM A638 Gr.660
- 28EN 58A
- 27Z10CNT18-11
- 26SAE 30304
- 26ASTM A538 / AMS 6514
- 26AISI 306
- 25Z15CN17-03
- 2410705MBU