Technical specifications of JIS heat resistance steel alloy SUH661 datasheet, Chemical compositions, SUH661 mechanical properties from Steelmaking, ESR melting,Hot blooming, Hot forging, Hot rolling, SUH661 Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - JIS G4311 -1991.We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
MATERIAL TECHNICAL DATA SHEET - JIS SUH661
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Heat resisting steel Austinite stainless steel
TECHNICAL SPECIFICATIONS: JIS G4311 -1991
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.08 ~ 0.16
Si (％): ≤ 1.00
Mn (％): 1.00 ~ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 20.0 ~ 22.5
Ni (％): 19.0 ~ 21.0
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.08 ~ 0.16
Si (％): ≤ 1.00
Mn (％): 1.00 ~ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 20.0 ~ 22.5
Ni (％): 19.0 ~ 21.0
Mo (%): 2.50 ~ 3.50
W (%): 2.00 ~ 3.00
Co (%): 18.50 ~ 21.0
Nb (%): 0.75 ~ 1.25
N (%): 0.10 ~ 0.20
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICE
Annealed: -
Annealed: -
Solution treated or Quenching: 1130 ~ 1200, rapid cooled
Ageging treated or Tempering: -
Condition: Solution treated
σb/≥ MPa: 690
σ0.2/≥ MPa: 315
δ ≥(％): 35
ф ≥ (％): 35
Hardness | HBW ≤: 248 min.
σb/≥ MPa: 690
σ0.2/≥ MPa: 315
δ ≥(％): 35
ф ≥ (％): 35
Hardness | HBW ≤: 248 min.
Suitable size (Diam. Thickness, Square size): ≤ 180 mm
Solution treated or Quenching: 1130 ~ 1200, rapid cooled
Ageging treated or Tempering: 780 ~ 830 X 4h, air cooled
Condition: Solution+ Ageing treated
σb/≥ MPa: 760
σ0.2/≥ MPa: 345
δ ≥(％): 30
ф ≥ (％): 30
Hardness | HBW ≤: 192 min.
σb/≥ MPa: 760
σ0.2/≥ MPa: 345
δ ≥(％): 30
ф ≥ (％): 30
Hardness | HBW ≤: 192 min.
Suitable size (Diam. Thickness, Square size): ≤ 75 mm
APPLICATION FIELD
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
APPLICATION FIELD
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
Pulp mill bleach systems
Seawater handling equipments
Tall oil distillation columns and equipments
Seawater handling equipments
Tall oil distillation columns and equipments
Heat-resistant steels are widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
Manufacturing technology - Smelting
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
Manufacturing technology - Smelting
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
PRODUCT DESCRIPTION
Round bar: Diam.1.0 ~ 850mm
Flat / Square bar: T10 ~ 350mm X W15 ~ 1200mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email: lh.steel@hotmail.com
Hot search：SUH661
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1