2024-11-21 09:32:00 Origin： Remark：0 Click：
Austenitic Stainless Steel F49 ESR refined Round bar, plate, S34565 Flat bar Hot forging, Hot rolling, Heat treatment, F49 Cold working or machined.
TECHNICAL DATA SHEET - F49
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: American high temperature alloy and other special alloy
CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 5.00 ~ 7.00
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 23.0 ~ 25.0
Nickel, Ni (％): 16.0 ~ 18.0
Molybdenum, Mo (％): 4.00 ~ 5.00
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 5.00 ~ 7.00
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 23.0 ~ 25.0
Nickel, Ni (％): 16.0 ~ 18.0
Molybdenum, Mo (％): 4.00 ~ 5.00
Cobalt, Co (%): -
Nitrogen, N (%): 0.40 ~ 0.60
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength, Rm ≥ MPa: 795
Yield strength, Rp0.2 ≥ MPa: 415
Elongation, A5 ≥ (％): 35
Elongation, A5 ≥ (％): 35
Reduction of area, ф ≥ (％): -
Hardness | HBW: 241
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Heat treating fixture, Furnace muffle, Nuclear reactor.
Turbine engine parts - mechanical gears, gear shaft, main axis, blade.
Mechanical parts - bolt and nut, fastener, Gas turbine, Turbine blade, Fuel nozzle.
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
PROFILES AND DIMENSIONS
Round bar (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 1000mm
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 3mm to 1000mm
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：F49