Valve steel S63019 datasheet, S63019 Chemical,S63019 properties from Steelmaking, ESR melt, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
MATERIAL TECHNICAL DATA SHEET - UNS S63019
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: SAE / UNS system exhaust valve Steel
CHEMICAL COMPOSITION (WEIGHT %)
C (%): 0.45 ~ 0.45
Si (%): ≤
Mn (%): 8.00 ~ 10.0
P (%) ≤: 0.045
S (%) ≤: 0.030
Cr (%): 20.0 ~ 22.0
Ni (%): 3.50 ~ 5.00
Mo (%): - 0.45
Mn (%): 8.00 ~ 10.0
P (%) ≤: 0.045
S (%) ≤: 0.030
Cr (%): 20.0 ~ 22.0
Ni (%): 3.50 ~ 5.00
Mo (%): - 0.45
W (%): 0.80 ~ 1.50
Nb (%): 1.80 ~ 2.50
N (%): 0.40 ~ 0.60
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: QT treated
Tensile strength, σb/≥ MPa: 950 ~ 1150
Yield strength, σ0.2/≥ MPa: 580
Elongation, δ ≥(%): 12.0
Elongation, δ ≥(%): 12.0
Reduction of area, ф ≥ (%): 15.0
Hardness | HB: -
FEATURES AND CLASSIFICATIONS
Valve steel is a subbranch of heat resistant steels, which is a special material for processing the vent valve & intake valve of combustion engines. This steel material is always under the high temperature 450 ~ 900℃ and also in the operating conditions of 3000~7000kPa explosion pressure. It longly stands up to the gas-fired high temperature corrosion, scouring of gasoline, diesel and also friction from valve seats. Hence, the valve steel material must have enough heat resistance, high temperature resistance corrosivity, inoxidizability, abrasive resistance and impact resistance under the highest working temperature.
Valve steel (gas valve steel) is suit for fabricating different types of valves. To improve the abrasive resistance and corrosion resistance, surface modified process can be used, such as surface alumetizing, bead welding hard alloy. Based on the pattern of organization, Valve steel is divided into martensitic type and austenitic type. The presentative martensitic valve steel is BS 381S34, BS 349S52 and austenitic valve steel BS 401S45, BS 443S65.
Valve steel (gas valve steel) is suit for fabricating different types of valves. To improve the abrasive resistance and corrosion resistance, surface modified process can be used, such as surface alumetizing, bead welding hard alloy. Based on the pattern of organization, Valve steel is divided into martensitic type and austenitic type. The presentative martensitic valve steel is BS 381S34, BS 349S52 and austenitic valve steel BS 401S45, BS 443S65.
FORMS AND SHAPES
Round bar (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1200mm X L1000 - 6000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1200mm X L1000 - 6000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search:S63019
Previous page:1345H/H13450
Last page:SUS403FB
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1