AMS 5629, a Martensitic precipitation hardening steel, 13-8Mo (UNS S13800) has excellent strength, high hardness, superior toughness, and good corrosion resistance

 

 RAW MATERIAL SPECIFICATIONS - Grade AMS 5629

MATERIAL CATEGORY: Martensitic precipitation hardening stainless steel, 13-8 stainless alloy (UNS S13800) is a martensitic precipitation-hardening stainless steel that has excellent strength, high hardness, superior toughness, and good corrosion resistance.

OFFICIAL TEST CERTIFICATE: issued by TUV - SGS -  BV
MATERIAL SPECIFICATIONS: ASTM A693 (2003)
CHEMICAL COMPOSITION (mass weight -%)
Carbon, C (%): ≤ 0.05
Silicon, Si (%): ≤ 0.10
Manganese, Mn (%): ≤ 0.20
Phosphorus, P (%)≤: 0.010
Sulfur, S (%)≤: 0.008
Chromium, Cr (%): 12.3 ~ 13.2
Nickel, Ni (%): 7.50 ~ 8.50
Molybdenum, Mo (%): 2.00 ~ 2.50
Aluminum, Al (%): 0.90 ~ 1.35, Nitrogen, N (%): ≤ 0.01
MECHANICAL PROPERTIES UNDER DIFFERENT AGEING TEMPERATURES
Solution treatment temperature and cooling ways: 1050 +/-15℃
Ageing teated: H1000, 540℃, 4h, air cooling
TS, σb≥/MPa: 1410
YS, σ0.2≥/MPa: 1312
EL, δ≥(%): 10.0
Hardness |HRC: 43
Ageing teated: H1025, 550℃, 4h, air cooling
TS, σb≥/MPa: 1275
YS, σ0.2≥/MPa: 1200
EL, δ≥(%): 11.0
Hardness |HRC: 41
Ageing teated: H1050, 565℃, 4h, air cooling
TS, σb≥/MPa: 1200
YS, σ0.2≥/MPa: 1135
EL, δ≥(%): 12.0
Hardness |HRC: 40
Ageing teated: H1100, 595℃, 4h, air cooling
TS, σb≥/MPa: 1030
YS, σ0.2≥/MPa: 930
EL, δ≥(%): 14.0
Hardness |HRC: 34
Ageing teated: H1150, 620℃, 4h, air cooling
TS, σb≥/MPa: 930
YS, σ0.2≥/MPa: 625
EL, δ≥(%): 14.0
Hardness |HRC: 30
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in solution annealed condition.
Final heat treatment - solution + ageing treated
TYPICAL APPLICATIONS
A high level of useful mechanical properties under severe environmental conditions. Alloy 13-8 Stainless Steel is used in aerospace components, landing gear, nuclear reactor components, petrochemical industry, injection molding equipment etc. Alloy 13-8
Stainless Steel in the annealed condition can be strengthened further by relatively low temperature heat treatment.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.0mm to 500mm
Square bar / Flat bar: 8mm to 800mm
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Other different shapes based on OEM.

TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: