Martensitic Steel AIR 9160C Z30C13 Round bar, flat bar, plate Z30C13 ESR melted, Hot forging, Grade Z30C13 Hot rolling, Heat treatment, cold machined.
TECHNICAL SPECIFICATION - AIR 9160C Grade Z30C13
Technical specification - DGA - AIR 9160/C - 1973
Official test certificate: issued by TUV - SGS
Material type: martensitic stainless steel
Chemical composition (mass weight - %)
Carbon, C (％): 0.25 ~ 0.32
Silicon, Si (％): ≤ 0.80
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (%): 12.0 ~ 14.0
Molybdenum, Mo (%): -
Nickel, Ni (%): ≤ 1.00
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: 880 ~ 1080
Yield strength, σ0.2/≥ MPa: 690
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥ (％): -
Impact, AK (J/cm2): -
Annealed hardness | HB: 262 ~ 326
Quenching, 990,+/-10 Deg, tempering 600, +/-5 Deg.
AVAILABLE FORMS AND DIMENSIONS
Round bar (Diameter): 1.5 mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 2000mm X Coil
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Technical specification - DGA - AIR 9160/C - 1973
Official test certificate: issued by TUV - SGS
Material type: martensitic stainless steel
Chemical composition (mass weight - %)
Carbon, C (％): 0.25 ~ 0.32
Silicon, Si (％): ≤ 0.80
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (%): 12.0 ~ 14.0
Molybdenum, Mo (%): -
Nickel, Ni (%): ≤ 1.00
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: 880 ~ 1080
Yield strength, σ0.2/≥ MPa: 690
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥ (％): -
Impact, AK (J/cm2): -
Annealed hardness | HB: 262 ~ 326
Quenching, 990,+/-10 Deg, tempering 600, +/-5 Deg.
AVAILABLE FORMS AND DIMENSIONS
Round bar (Diameter): 1.5 mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 2000mm X Coil
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Previous page：JIS G4309 SUS310S
Last page：Z2CN18-10
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1