Z2CN18-10
2016-12-28 09:19:37 Origin： Remark：0 Click：
AIR 9160/C Austenitic Stainless Steel Z2CN18-10 Round bar, Flat bar, Plate, and Forgings Z2CN18-10 Stock Available, Hot forging/rolling, Heat treatment
TECHNICAL SPECIFICATION - AIR 9160C Grade Z2CN18-10
TECHNICAL SPECIFICATION - DGA - AIR 9160/C - 1973
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (%): 17.0 ~ 18.0
Molybdenum, Mo (%): -
Nickel, Ni (%): 9.00 ~ 10.0
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength, Rm ≥ MPa: 440 ~ 640
Yield strength, Rp0.2 ≥ MPa: 180
Elongation, 5A ≥(％): -
Reduction of area, ф ≥ (％): 45.0
Impact, AK (J/cm2): -
Annealed hardness | HB: -
Yield strength, Rp0.2 ≥ MPa: 180
Elongation, 5A ≥(％): -
Reduction of area, ф ≥ (％): 45.0
Impact, AK (J/cm2): -
Annealed hardness | HB: -
Quenching/Solution treated, 1050,+/-10 Deg,.
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5 to 500mm
Square bar / Flat bar: 10 to 620mm
Steel strip: T0.20 ~ 3mm X W10 ~ 1200mm X Coil
Round bar (Diameter): 5.5 to 500mm
Square bar / Flat bar: 10 to 620mm
Steel strip: T0.20 ~ 3mm X W10 ~ 1200mm X Coil
Sheet & Plate: T3.0 ~ 30 X W10 ~ 1500 X L1000 ~ 6000mm
Forging piece: stepped shafts /other different shapes based on OEM.
Forging piece: stepped shafts /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：Z2CN18-10
Previous page：AIR 9160C Z30C13
Last page：38XH3BA
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1