DGA - AIR 9160/C - 1973 Austenitic Steel Z10CNT18-11 Round bar, flat bar, plate, sheet, wire rod ESR melted, Hot forging / rolling, Heat treatment
TECHNICAL DATASHEET - AIR 9160C Grade Z10CNT18-11
TECHNICAL SPECIFICATION - DGA - AIR 9160/C - 1973
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.12
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 2.00
Phosphorus, P (%) ≤: 0.035
Sulfur, S (%) ≤: 0.025
Carbon, C (%): ≤ 0.12
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 2.00
Phosphorus, P (%) ≤: 0.035
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): 17.0 ~ 19.0
Molybdenum, Mo (%): -
Nickel, Ni (%): 10.0 ~ 13.0
Titanium, Ti (%): 5 X C ~ 0.80
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength, Rm ≥ MPa: 490 ~ 690
Yield strength, Rp0.2 ≥ MPa: 220
Elongation, A5 ≥ (%): -
Reduction of area, Z ≥ (%): 40.0
Impact, AKv (J/cm2): -
Annealed hardness | HB: 262 ~ 326
Tensile strength, Rm ≥ MPa: 490 ~ 690
Yield strength, Rp0.2 ≥ MPa: 220
Elongation, A5 ≥ (%): -
Reduction of area, Z ≥ (%): 40.0
Impact, AKv (J/cm2): -
Annealed hardness | HB: 262 ~ 326
uenching/Solution treated, 1080,+/-10 Deg, tempering 600, +/-5 Deg.
AVAILABLE SIZES AND SHAPES
Round bar (Diameter): 5.5 ~ 550mm
Square bar / Flat bar: 6 ~ 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 1200mm X Coil
Forging piece: stepped shafts, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search:Z10CNT18-11
Previous page:HS6-5-2-5
Last page:Z6CND15-07
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1