Z6CNUD15-04
2025-04-18 15:02:00 Origin： Remark：0 Click：

Description Z6CNUD15-04 Stockist, Inventory Z6CNUD15-04 Round bar, flat bar, and forgings, ESR ingot, Hot forging, Hot rolling, Heat treatment

TECHNICAL DATA SHEET - Z6CNUD15-04

TECHNICAL SPECIFICATION: DGA - AIR 9160/C - 1973

OFFICIAL TEST CERTIFICATE: issued by TUV - SGS

MATERIAL TYPE: Stainless steel

Customs HS Code - 72221100 / 72221900

Stocklist & Inventory - Diameter 55mm / 100mm

CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025

Chromium, Cr (%): 13.5 ~ 15.5

Molybdenum, Mo (%): 1.00 ~ 1.60

Nickel, Ni (%): 3.00 ~ 5.00

Copper, Cu (%): 2.50 ~ 4.50

MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE

Tensile strength,σb/≥ MPa: 930 ~ 1130
Yield strength, σ0.2/≥ MPa: 690
Elongation, δ ≥(％): 12.0
Reduction of area, ф ≥ (％): -
Impact, AK (J/cm2): -
Annealed hardness | HB: -

Quenching/Solution treated, 1050,+/-10 Deg, tempering/ageing 550, +/-5 Deg.

FORMS AND DIMENSIONS
Rod / round bar / disc (diameter): 5.5 mm to 900mm
Square bar / flat bar: 8mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 200mm X Coil
Forging piece: stepped shaft, and other different shapes based on OEM.

TECHNICAL SALES ASSISTANCE

If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com

Hot search：Z6CNUD15-04

Previous page：Z6CND15-07
Last page：E-Z6NCT25

Share to：

Z6CNUD15-04
2025-04-18 15:02:00 Origin： Remark：0 Click：

Total list

Monthly rank

Z6CNUD15-04 2025-04-18 15:02:00 Origin： Remark：0 Click：

Total list

Monthly rank

Z6CNUD15-04
2025-04-18 15:02:00 Origin： Remark：0 Click：