Air 9160/C Nickel 25% alloy Steel E-Z6NCT25 Round bar, Flat bar, Forgings, Stock E-Z6NCT25 VIM, Hot forging, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - AIR 9160C type E-Z6NCT25
TECHNICAL SPECIFICATION: DGA - AIR 9160/C - 1973
Stock Available - Round bar Diam. 10 ~ 180mm
SPECIAL MELTING PROCESS - EAF + AOD + ESR / VIM + ESR / VAR
HS Code For Customs - 72221100 / 72221900 / 72222000
MATERIAL TYPE - Stainless steel
CHEMICAL COMPOSITIONS ( mass weight % )
Carbon, C (%): ≤ 0.08
Silicon, Si (%): 0.40 ~ 1.00
Manganese, Mn (%): 1.00 ~ 2.00
Phosphorus, P (%) ≤: 0.030
Sulfur, S (%) ≤: 0.015
CHEMICAL COMPOSITIONS ( mass weight % )
Carbon, C (%): ≤ 0.08
Silicon, Si (%): 0.40 ~ 1.00
Manganese, Mn (%): 1.00 ~ 2.00
Phosphorus, P (%) ≤: 0.030
Sulfur, S (%) ≤: 0.015
Chromium, Cr (%): 13.5 ~ 16.0
Molybdenum, Mo (%): 1.00 ~ 1.50
Nickel, Ni (%): 24.0 ~ 27.0
Vanadium, V (%): 0.10 ~ 0.50
Aluminum, Al (%): ≤ 0.35
Titanium, Ti (%): 1.90 ~ 2.30
Boron, B (%): 0.0010 ~ 0.010
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength, Rm ≥ MPa: 960 ~ 1150
Yield strength, Rp0.2 ≥ MPa: 660
Elongation, A5 ≥ (%): 10.0
Reduction of area, Z ≥ (%): -
Impact strength, AKv (J/cm2): -
Annealed hardness | HB: 262 min.
Tensile strength, Rm ≥ MPa: 960 ~ 1150
Yield strength, Rp0.2 ≥ MPa: 660
Elongation, A5 ≥ (%): 10.0
Reduction of area, Z ≥ (%): -
Impact strength, AKv (J/cm2): -
Annealed hardness | HB: 262 min.
Quenching/Solution treated, 900,+/-10 Deg, tempering/ageing 720, +/-5 Deg.
AVAILABLE FORMS AND DIMENSIONS
Round bar & disc (diameter): 5.5 ~ 800mm
Square bar / flat bar: 10 ~ 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 1000mm X Coil
AVAILABLE FORMS AND DIMENSIONS
Round bar & disc (diameter): 5.5 ~ 800mm
Square bar / flat bar: 10 ~ 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 1000mm X Coil
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search:E-Z6NCT25
Previous page:Z6CNUD15-04
Last page:JIS G4309 SUS316
Total list
Monthly rank
- 58Z15CN17-03
- 47ASTM A565 type 616HT
- 39X35CrMo17
- 3510705MBU
- 31FV535
- 26P550
- 24Z8CND17-04
- 24X2Cr11 / 1.4003
- 23X8CrMnN18-18
- 23ASTM A638 Gr.660