UNS N08825
2017-02-27 10:58:50 Origin： Remark：0 Click：
Technical specifications of ASTM B564-04 Nickel alloy forgings Grade UNS N08825 data sheet,UNS N08825 Chemical composition,UNS N08825 mechanical properties from Steelmaking, ESR melted, Blooming, Forging, UNS N08825 Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - ASTM B564-04 Grade UNS N08825
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ni-Ti-Cr-Mo-Cu Alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): ≤ 0.50
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.030
Cr (％): 19.5 ~ 23.5
Ni (％): 38.0 ~ 46.0
Mo (％): 2.50 ~ 3.50
Cu (%): 1.50 ~ 3.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.030
Cr (％): 19.5 ~ 23.5
Ni (％): 38.0 ~ 46.0
Mo (％): 2.50 ~ 3.50
Cu (%): 1.50 ~ 3.00
Al (%): ≤ 0.20
Ti (%): 0.60 ~ 1.20
Ce (%): -
Zr (%): -
Y (%): -
Nb (%): -
Co (%): -
V (%): -
N (%): -
B (%): -
W (%): -
W (%): -
Ta (%): -
Fe (%): 22.0 min.
MECHANICAL PROPERTIES
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 586
Yield strength, σ0.2/≥ MPa: 241
Elonghation, δ ≥(％): 30.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Fe (%): 22.0 min.
MECHANICAL PROPERTIES
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 586
Yield strength, σ0.2/≥ MPa: 241
Elonghation, δ ≥(％): 30.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. - Email: lh.steel@hotmail.com
Previous page：UNS N06110
Last page：Incoloy 825 / N08825
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1