ASTM B564-04 Nickel alloy 2.4605 Round bar, flat bar, wire rod N06059 sheet ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test,
TECHNICAL DATA SHEET - Grade Alloy 59 & 2.4605 & N06059
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Low-carbon -Ni-Cr-Mo Alloy
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.010
MATERIAL CATEGORY: Low-carbon -Ni-Cr-Mo Alloy
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.010
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.015
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): Balance
Molybdenum, Mo (％): 15.0 ~ 16.5
Cooper, Cu (%): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.015
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): Balance
Molybdenum, Mo (％): 15.0 ~ 16.5
Cooper, Cu (%): ≤ 0.50
Aluminum, Al (%): 0.10 ~ 0.40
Titanium, Ti (%): -
Cerium, Ce (%): ≤ 0.30
Niobium, Nb (%): -
Cobalt, Co (%): -
Vanadium, V (%): -
Nitrogen, N (%): -
Boron, B (%): -
Ferrum, Fe (%): 1.50 max.
TYPICAL MECHANICAL PROPERTIES
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 310
Elonghation, δ ≥(％): 45.0
PRODUCT DESCRIPTION
The alloy is usually produced by VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TYPICAL MECHANICAL PROPERTIES
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 310
Elonghation, δ ≥(％): 45.0
PRODUCT DESCRIPTION
The alloy is usually produced by VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：Alloy 59/2.4605/N06059
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1