ASTM A437 type B4B
2017-03-14 08:47:49 Origin： Remark：0 Click：
Stock Available ASTM A437 Gr.B4B Round bar, Flat bar, Bolts, Nuts A437 type B4B ESR melting, UT, Hot forging / rolling, Heat treatment
TECHNICAL DATA SHEET - ASTM A437 type B4B
MATERIAL STANDARDS: ASTM A437 - 2012
STOCK AVAILABLE - Round bar Diam. 20 ~ 280mm, ESR ingot, Forging blank, Flat bar
CHEMICAL COMPOSITION ( mass weight - %)
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): 0.20 ~ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (%): 0.90 ~ 1.25
Tungsten, W (%): 0.90 ~ 1.25
Vanadium, V (%): 0.20 ~ 0.30
Aluminum, Al (%): ≤ 0.05
Titanium, Ti (%): ≤ 0.05
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): 0.20 ~ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (%): 0.90 ~ 1.25
Tungsten, W (%): 0.90 ~ 1.25
Vanadium, V (%): 0.20 ~ 0.30
Aluminum, Al (%): ≤ 0.05
Titanium, Ti (%): ≤ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Quenched 1025 ~ 1050℃, oil cooled
Tempered 650℃ min., air cooled
Annealed hardness: 321 max.
Tensile strength,Rm ≥ MPa: 970
Yield strength, Rp0.2 ≥ MPa: 720
Elongation, A5 ≥ (％): 13.0
Hardness under QT condition: 352 max.
Impact, AKV: 14J min.
Condition: Quenched 1025 ~ 1050℃, oil cooled
Tempered 650℃ min., air cooled
Annealed hardness: 321 max.
Tensile strength,Rm ≥ MPa: 970
Yield strength, Rp0.2 ≥ MPa: 720
Elongation, A5 ≥ (％): 13.0
Hardness under QT condition: 352 max.
Impact, AKV: 14J min.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF+LF+AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - quenched and tempered + SRA.
The alloy is usually produced by EAF+LF+AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - quenched and tempered + SRA.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE & DIMENSIONS
Round bar & Disc (diameter): 5.5 to 850mm
Square bar / flat bar: 10 to 600mm
Plate: T60 ~ 400 X W60 ~ 1000 X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Round bar & Disc (diameter): 5.5 to 850mm
Square bar / flat bar: 10 to 600mm
Plate: T60 ~ 400 X W60 ~ 1000 X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified product engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified product engineers.
Hot search：
Previous page：Haynes alloy 230
Last page：ASTM A437 Gr.B4C
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1