NF X1CrNiMoCu12-7-3
2017-03-21 09:38:06 Origin： Remark：0 Click：
Material technical specifications of NF EN 10088-2 2005 type X1CrNiMoCu12-7-3 stainless steel plate and strip X1CrNiMoCu12-7-3 datasheet, NF EN X1CrNiMoCu12-7-3 Chemical compositions, mechanical properties from Steelmaking, ESR melting, Hot blooming, UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF EN 10088-2 2005. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL SPECIFICATION & DATASHEET - NF EN X1CrNiMoCu12-7-3
TYPE OF STEEL: Martensitic and precipitation hardening steel
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel Plate and Strip
Technical standards: NF EN 10088-2 2005
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.020
Si (％): ≤ 0.50
Mn (％): ≤ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 11.0 ~ 13.0
Mo (%): 2.30 ~ 2.80
Ni (％): 6.00 ~ 7.00
Cu (%): 0.20 ~ 0.80
N (%): 0.020 max.
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: cold rolled steel strip
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: cold rolled steel strip
Annealed hardness: -
Condition: QT650
Tensile strength,σb/≥ MPa: 750 ~ 950
Yield strength, σ0.2/≥ MPa: 550
Elongation, δ ≥(％): 15.0
Tensile strength,σb/≥ MPa: 750 ~ 950
Yield strength, σ0.2/≥ MPa: 550
Elongation, δ ≥(％): 15.0
QT hardness: 300 max.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE
Heavy/middle plate via hot rolled: T3 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 3mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 600mm X L (or in coil form)
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE
Heavy/middle plate via hot rolled: T3 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 3mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 600mm X L (or in coil form)
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Email: lh.steel@hotmail.com
Hot search：NF X1CrNiMoCu12-7-3
Previous page：Haynes 242
Last page：SKC31
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1