Haynes HR-160
2017-03-22 10:22:07 Origin： Remark：0 Click：
Technical specifications of ASTM B564-04 Nickel alloy forgings Grade Haynes HR-160 data sheet, Chemical composition,Grade Haynes HR-160 mechanical properties from Steelmaking,ESR melted, Blooming, Haynes HR-160 Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Haynes HR-160
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ni-Co-Cr-Si Alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
MATERIAL CATEGORY: Ni-Co-Cr-Si Alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
Si (％): 2.40 ~ 3.00
Mn (％): ≤ 1.50
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 19.0 ~ 23.0
Ni (％): Remainder
Mo (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 19.0 ~ 23.0
Ni (％): Remainder
Mo (％): ≤ 1.00
Cu (%): -
Al (%): -
Ti (%): 0.20 ~ 0.80
Ce (%): 27.0 ~ 33.0
Nb (%): ≤ 1.00
Co (%): -
V (%): -
N (%): -
B (%): -
W (%): ≤ 1.00
Fe (%): 3.5 max.
MECHANICAL PROPERTIES
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 620
Yield strength, σ0.2/≥ MPa: 240
Elonghation, δ ≥(％): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
MECHANICAL PROPERTIES
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 620
Yield strength, σ0.2/≥ MPa: 240
Elonghation, δ ≥(％): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email: lh.steel@hotmail.com
Previous page：N12160
Last page：C90U/C90E2U
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1