Description S32205 Stocklist, Inventory S32205 Suppliers, Ex-stock S32205 Specifications from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treated, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL DATA SHEET - Grade UNS 32205
MATERIAL CATEGORY - 22Cr-5Ni-3Mo-N Austenite-Ferrite type
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION ( Mass weight % )
C (%): ≤ 0.030
Si (%): ≤ 1.00
Mn (%): ≤ 2.00
P (%)≤: 0.030
S (%)≤: 0.020
Cr (%): 22.0 ~ 23.0
Ni (%): 4.50 ~ 6.50
Mo (%): 3.00 ~ 3.50
N (%): 0.14 ~ 0.20
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Si (%): ≤ 1.00
Mn (%): ≤ 2.00
P (%)≤: 0.030
S (%)≤: 0.020
Cr (%): 22.0 ~ 23.0
Ni (%): 4.50 ~ 6.50
Mo (%): 3.00 ~ 3.50
N (%): 0.14 ~ 0.20
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: plate,sheet,strip
Condition: annealing
Tensile strength, σb/MPa: 620
Yield strength, σ0.2/MPa: 450
Elongation, δ(%): 25
Elongation, δ(%): 25
Reduction of area, ф (%): -
Hardness | HRC(HBS): 32
Form: bar
Condition: annealing
σb/MPa: 620
σ0.2/MPa: 448
δ(%): 25
ф(%): -
δ(%): 25
ф(%): -
Hardness | HRC(HBS): (290)
Form: tube
Condition: annealing
σb/MPa: 620
σ0.2/MPa: 450
δ(%): 25
ф(%): -
δ(%): 25
ф(%): -
Hardness | HRC(HBS): 30.5
Form: pipe
Condition: annealing
σb/MPa: 620
σ0.2/MPa: 450
δ(%): 25
ф(%): -
δ(%): 25
ф(%): -
Hardness | HRC(HBS): 30.5
AVAILABILITY
Round bar / flat bar / strip / square bar / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / strip / square bar / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 10mm to 500mm
Plate / Sheet steel / Steel strip: 0.5mm to 400mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 10mm to 500mm
Plate / Sheet steel / Steel strip: 0.5mm to 400mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search:S32205
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1